Capacitor with conductively doped Si-Ge alloy electrode

ABSTRACT

Capacitors and methods of forming capacitors are disclosed. In one implementation, a capacitor comprises a capacitor dielectric layer comprising Ta 2 O 5  formed over a first capacitor electrode. A second capacitor electrode is formed over the Ta 2 O 5  capacitor dielectric layer. Preferably, at least a portion of the second capacitor electrode is formed over and in contact with the Ta 2 O 5  in an oxygen containing environment at a temperature of at least about 175° C. Chemical vapor deposition is one example forming method. The preferred second capacitor electrode comprises a conductive metal oxide. A more preferred second capacitor electrode comprises a conductive silicon comprising layer, over a conductive titanium comprising layer, over a conductive metal oxide layer. A preferred first capacitor electrode comprises a conductively doped Si—Ge alloy. Preferably, a Si 3 N 4  layer is formed over the first capacitor electrode. DRAM cells and methods of forming DRAM cells are disclosed.

TECHNICAL FIELD

[0001] This invention relates to capacitors, to methods of forming capacitors, and to DRAM cells.

BACKGROUND OF THE INVENTION

[0002] As DRAMs increase in memory cell density, there is a continuing challenge to maintain sufficiently high storage capacitance despite decreasing cell area. Additionally, there is a continuing goal to further decrease cell area. One principal way of increasing cell capacitance is through cell structure techniques. Such techniques include three-dimensional cell capacitors, such as trenched or stacked capacitors.

[0003] Yet as feature size continues to become smaller and smaller, development of improved materials for cell dielectrics as well as the cell structure are important. The feature size of 256 Mb DRAMs will be on the order of 0.25 micron, and conventional dielectrics such as SiO₂ and Si₃N₄ might not be suitable because of small dielectric constants.

[0004] Highly integrated memory devices, such as 256 Mbit DRAMs, are expected to require a very thin dielectric film for the 3-dimensional capacitor of cylindrically stacked or trench structures. To meet this requirement, the capacitor dielectric film thickness will be below 2.5 nm of SiO₂ equivalent thickness. Chemical vapor deposited (CVD) Ta₂O₅ films are considered to- be very promising cell dielectric layers for this purpose, as the dielectric constant of Ta₂O₅ is approximately three times that of conventional Si₃N₄ capacitor dielectric layers. However, one drawback associated with Ta₂O₅ dielectric layers is undesired leakage current characteristics. Accordingly, although Ta₂O₅ material has inherently higher dielectric properties, as-deposited Ta₂O₅ typically produces unacceptable results due to leakage current.

[0005] Densification of Ta₂O₅ as deposited has been reported to significantly improve the leakage characteristics of such layers to acceptable levels. Prior art densification of such layers includes exposing the Ta₂O₅ layer to extreme annealing and oxidizing conditions. The anneal drives any carbon present out of the layer and advantageously injects additional oxygen into the layer such that the layer uniformly approaches a stoichiometry of five oxygen atoms for every two tantalum atoms. The oxygen anneal is commonly conducted at a temperature of from about 400° C. to about 1000° C. utilizing an ambient comprising an oxygen containing gas. The oxygen containing gas commonly comprises one or more of O₃, NO, N₂O and O₂. The oxygen containing gas is typically flowed through a reactor at a rate of from about 0.5 slm to about 10 slm.

[0006] The Ta₂O₅ layer is typically from about 40 angstroms to about 150 angstroms thick and can be either amorphous or crystalline. Ta₂O₅ is generally amorphous if formed below 600° C. and will be crystalline if formed, or later processed, at or above 600° C. Typically, a Ta₂O₅ layer is deposited as an amorphous layer and the above-described oxygen anneal is conducted at a temperature of 600° C. or greater to convert the amorphous Ta₂O₅ layer to a crystalline layer. Undesirably, however, such has a tendency to form an SiO₂ layer intermediate or between the polysilicon and Ta₂O₅. Further and regardless, a thin SiO₂ layer will also typically inherently form during the Ta₂O₅ deposition due to the presence of oxygen at the polysilicon layer interface. It would be desirable to remove or eliminate this SiO₂ layer intermediate the Ta₂O₅ and polysilicon layers, yet allow for such desired densification.

[0007] One prior art technique reported includes exposing the polysilicon layer to rapid thermal nitridation prior to subsequent deposition of the Ta₂O₅ layer. Such are reported by Kamiyama et al., “Ultrathin Tantalum Oxide Capacitor Dielectric Layers Fabricated Using Rapid Thermal Nitridation prior to Low Pressure Chemical Vapor Deposition”, J. Electrochem. Soc., Vol. 140, No. 6, June 1993 and Kamiyama et al., “Highly Reliable 2.5 nm Ta₂O₅ Capacitor Process Technology for 256 Mbit DRAMs”, 830-IEDM 91, pp. 32.2.1-32.2.4. Such rapid thermal nitridation includes exposing the subject polysilicon layer to temperatures of from 800° C. to 1100° C. for sixty seconds in an ammonia atmosphere at atmospheric pressure. The nitride layer acts as a barrier layer to oxidation during Ta₂O₅ deposition and subsequent high temperature densification processes to prevent oxidation of the underlying polysilicon electrode. These processes do however have several drawbacks, including the undesired high temperature cycling and formation of a fairly thick native SiO₂ on the nitride in series with the Ta₂O₅, all of which adversely effects the realization of high capacitance promised by inherent Ta₂O₅ layers.

SUMMARY OF THE INVENTION

[0008] The invention comprises capacitors, methods of forming capacitors and DRAM circuitry. In one implementation, a capacitor comprises a capacitor dielectric layer comprising Ta₂O₅ formed over a first capacitor electrode. A second capacitor electrode is formed over the Ta₂O₅ capacitor dielectric layer. Preferably, at least a portion of the second capacitor electrode is formed over and in contact with the Ta₂O₅ in an oxygen containing environment at a temperature of at least about 175° C. Chemical vapor deposition is one example forming method. The preferred second capacitor electrode comprises a conductive metal oxide. A more preferred second capacitor electrode comprises a conductive silicon comprising layer, over a conductive titanium comprising layer, over a conductive metal oxide layer. A preferred first capacitor electrode comprises a conductively doped Si—Ge alloy. Preferably, a Si₃N₄ layer is formed over the first capacitor electrode.

BRIEF DESCRIPTION OF THE DRAWINGS

[0009] Preferred embodiments of the invention are described below with reference to the following accompanying drawings.

[0010]FIG. 1 is a diagrammatic depiction of a capacitor stack in accordance with one aspect of the invention.

[0011]FIG. 2 is a diagrammatic depiction of another capacitor stack in accordance with one aspect of the invention.

[0012]FIG. 3 is a diagrammatic depiction of yet another capacitor stack in accordance with one aspect of the invention.

[0013]FIG. 4 is a diagrammatic depiction of still another capacitor stack in accordance with one aspect of the invention.

[0014]FIG. 5 is a view an alternate embodiment semiconductor wafer fragment in accordance with the invention.

DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS

[0015] This disclosure of the invention is submitted in furtherance of the constitutional purposes of the U.S. Patent Laws “to promote the progress of science and useful arts” (Article 1, Section 8).

[0016]FIG. 1 diagrammatically depicts a capacitor stack 10 which would be formed over a substrate. To aid in interpretation of the claims that follow, the term “semiconductive substrate” is defined to mean any construction comprising semiconductive material, including, but not limited to, bulk semiconductive materials such as a semiconductive wafer (either alone or in assemblies comprising other materials thereon), and semiconductive material layers (either alone or in assemblies comprising other materials). The term “substrate” refers to any supporting structure, including but not limited to, the semiconductive substrates described above.

[0017] Capacitor 10 comprises a first capacitor electrode 12, a capacitor dielectric layer 14, and a second capacitor electrode 15. In the illustrated example, first capacitor electrode 12 comprises silicon material 16, such as elemental silicon in polycrystalline form which is suitably conductively doped with desired dopant impurities. Such can be formed, for example, by chemical vapor deposition using SiH₄ as a precursor gas at a temperature of 535° C. and a pressure of 200 mTorr. Doping can occur during or after deposition. An example preferred thickness range for layer 12 is from 400 Angstroms to 1000 Angstroms. Electrode 12 could of course constitute some other conductive material. Further, electrode 12 could comprise a composite of conductive materials, such as by way of example only Ru or RuO_(x) formed over conductively doped silicon.

[0018] Capacitor dielectric layer 14 is preferably formed over and in contact with electrode 12, and preferably comprises Ta₂O₅ material 18. Where electrode 12 comprises silicon, an intervening oxidation barrier layer (not shown) is ideally provided intermediate the Ta₂O₅ and silicon. Example conductive oxidation barrier layers include RuO_(x) and Ru. Ta₂O₅ can be deposited by low pressure chemical vapor deposition utilizing Ta(C₃H₅)₅, O₂ and N₂ as precursor gases. Example flow rates are 120 sccm; 2-5 slm; and 2-5 slm, respectively. An example temperature is 410° C., with an example pressure being from 200 to 400 mTorr. An example deposition thickness is from 60 to 90 Angstroms, with 70 Angstroms being preferred. The Ta₂O₅ layer is thereafter preferably subjected to a high temperature oxidation anneal by any one of the following processes, or other processes. In a first, rapid thermal processing is conducted over 40 seconds up to a temperature of 850° C. in a N₂O ambient, with pressure being 660 Torr. Processing continues at 850° C. and 660 Torr for one minute. In a second process, furnace heating is conducted to 800° C. at a temperature increase rate of 7° C./min. in a N₂O ambient, with pressure remaining at atmospheric and the wafer being maintained at 800° C. for 30 minutes. In a third, a higher pressure oxidation is conducted at 800° C. for 30 minutes in a N₂O atmosphere at a pressure from 1 to 3 atmospheres, with the temperature being ramped to 800° C. at an approximate rate of 15° C./min.

[0019] Second capacitor electrode 15 is preferably formed over and in contact with Ta₂O₅ material 18 of capacitor dielectric layer 14. Such preferably is formed in an oxygen-containing environment at a temperature of at least about 175° C. Second capacitor electrode 14 preferably comprises a conductive metal oxide material 20 formed to a thickness of from about 400 Angstroms to about 1000 Angstroms. In the context of this document, a conductive metal oxide is any oxide having a resistance of less than or equal to about microohms.cm. Example materials include RuO₂, IrO₂, SnO₂, In₂O₃:SnO₂, VO₃, CuO, Cu₂O, and mixtures thereof. RuO₂ and IrO₂ are more preferred. An example process for forming such conductive metal oxide is by chemical vapor deposition. For RuO_(x), an example deposition process would be conducted at a pressure of 1 Torr and a temperature of 175° C., with precursor feeds of Ru(tricarbonyl cyclohexdienyl) at 300 sccm and O₂ at 300 sccm.

[0020] Referring to FIG. 2, a second embodiment capacitor stack 10 a is shown. Like numerals from the first described embodiment are utilized where appropriate, with differences being indicated by the suffix “a” or with different numerals. Here, second capacitor electrode 15 a comprises a conductive silicon comprising layer 23 formed over and in contact with a conductive titanium comprising layer 22 (i.e., Ti or TiN), formed over and in contact with conductive metal oxide layer 20 a. Conductive metal oxide layer 20 a is also formed over and preferably in contact with Ta₂O₅ material 18 of capacitor dielectric layer 14. Accordingly, second capacitor electrode 15 a comprises both conductive silicon and a conductive metal oxide. A titanium comprising layer 22 is provided intermediate conductive metal oxide layer 20 a and conductive silicon layer 23. The preferred material for titanium-comprising layer 22 is TiN formed by chemical vapor deposition using an organic precursor. An example process utilizes precursors of ((CH₃)₂N)₄Ti at 150 sccm and N₂ at 80 sccm at a temperature of 420° C. and a pressure of 0.7 Torr. Silicon layer 23 preferably comprises conductively doped elemental polycrystalline silicon, with thus both the first and second capacitor electrodes comprising silicon. An example thickness for TiN layer 22 is from 150 Angstroms to 300 Angstroms. An example thickness for silicon layer 23 is from 400 Angstroms to 1000 Angstroms.

[0021] Yet another alternate embodiment capacitor stack 10 b is shown in FIG. 3. Like numerals from the first described embodiments are utilized where appropriate, with differences being indicated by the suffix “b” or with different numerals. Here, silicon material 16 b of first capacitor electrode 12 b is subjected to rapid thermal nitridation to form a silicon nitride layer 26 atop material 16 b and in contact with Ta₂O₅ material 18. Thereby, the capacitor dielectric layer 14 b essentially comprises a combination of the Ta₂O₅ and Si₃N₄. The nitridation is ideally conducted prior to formation of the Ta₂O₅, and functions as a diffusion restricting or barrier layer to formation of SiO₂ during deposition of Ta₂O₅ material 18. Thickness of layer 26 is preferably from 30 Angstroms to 60 Angstroms. Exemplary rapid thermal nitridation conditions include exposing the substrate to a NH₃ atmosphere at a flow rate of from about 10 to 20 sccm for 20 seconds at atmospheric pressure and 900-950° C. In the context of this document, rapid thermal nitridation is intended to define any process where a substrate is ramped to a temperature of at least 900° C. at a rate of 20° C./sec in a nitrogen containing environment.

[0022] Second capacitor electrode 15 b is formed to provide silicon both as polycrystalline silicon and as a silicide. Specifically, a silicide layer 24 is formed over silicon layer 23 b. Example techniques include a refractory metal deposition and conventional salicide process, or direct chemical vapor deposition of a silicide. Example precursor gases for chemical vapor depositing WSi_(x) include WF₆ and WSH₄. An example preferred thickness for silicide layer 24 is from about 300 Angstroms to 600 Angstroms.

[0023] Still a further alternate embodiment capacitor stack 10 c is described with reference to FIG. 4. Like numerals from the first described embodiments have been utilized where appropriate, with differences being indicated by the suffix “c” or with different numerals. Here, first capacitor electrode 12 c comprises a conductively doped silicon-germanium alloy material 16 c.

[0024] In each of the above described preferred embodiments where at least one of the first and second capacitor electrodes comprises titanium, no titanium-comprising material of either the first and second capacitor electrodes is formed in contact with the Ta₂O₅ material of the capacitor dielectric layer. Where the capacitor dielectric layer comprises Ta₂O₅, preferably such effectively gets heated in an oxygen rich atmosphere during top electrode deposition, which can minimize oxygen vacancy content in the Ta₂O₅. Where a conductive metal oxide is formed in contact with Ta₂O₅, reduction of the Ta₂O₅ can be avoided or at least reduced.

[0025]FIG. 5 depicts implementation of the invention in fabrication of DRAM circuitry. A wafer fragment 31 comprises two memory cells, with each comprising a capacitor 36 and a shared bit contact 46. Capacitors 36 electrically connect with substrate diffusion regions 34 through silicide regions 33. For simplicity, capacitors 36 are shown as comprising a first capacitor electrode 38, a capacitor dielectric layer 40, and a second capacitor electrode/cell plate 42. Such can be fabricated of materials described above, preferably to include silicon, barrier layers metal oxide, and a high K oxygen containing capacitor dielectric layers such as Ta₂O₅. Processing preferably occurs as described above. A dielectric layer 44 is formed over second capacitor plate 42. A bit line 47 is fabricated in electrical connection with bit contact 46. Word lines 48 are fabricated to enable selective gating of the capacitors relative to bit contact 47.

[0026] In compliance with the statute, the invention has been described in language more or less specific as to structural and methodical features. It is to be understood, however, that the invention is not limited to the specific features shown and described, since the means herein disclosed comprise preferred forms of putting the invention into effect. The invention is, therefore, claimed in any of its forms or modifications within the proper scope of the appended claims appropriately interpreted in accordance with the doctrine of equivalents. 

1. A capacitor comprising: a first capacitor electrode; a capacitor dielectric layer comprising Ta₂O₅ over the first capacitor electrode; and a second capacitor electrode over the Ta₂O₅ capacitor dielectric layer, the second capacitor electrode comprising a conductive metal oxide in contact with the Ta₂O₅.
 2. The capacitor of claim 1 wherein the second capacitor electrode comprises titanium in addition to the conductive metal oxide.
 3. The capacitor of claim 2 wherein the titanium comprises elemental titanium.
 4. The capacitor of claim 2 wherein the titanium comprises TiN.
 5. The capacitor of claim 1 wherein the second capacitor electrode comprises titanium and silicon in addition to the conductive metal oxide.
 6. The capacitor of claim 5 wherein the silicon is present both as polycrystalline silicon and as silicide.
 7. The capacitor of claim 1 wherein the first capacitor electrode comprises silicon.
 8. The capacitor of claim 1 wherein the first capacitor electrode comprises elemental silicon.
 9. The capacitor of claim 1 wherein the Ta₂O₅ is formed in contact with the first capacitor electrode.
 10. The capacitor of claim 1 wherein the conductive metal oxide is selected from the group consisting of RuO₂, IrO₂ and mixtures thereof.
 11. A method of forming a capacitor comprising: forming a first capacitor electrode over a substrate; forming a capacitor dielectric layer comprising Ta₂O₅ over the first capacitor electrode; and chemical vapor depositing a conductive metal oxide onto the Ta₂O₅.
 12. The method of claim 11 wherein the first capacitor electrode is formed to comprise silicon, and further comprising rapid thermal nitridizing the first capacitor electrode and forming a silicon nitride layer, the Ta₂O₅ of the capacitor dielectric layer being formed in contact with the silicon nitride.
 13. The method of claim 11 comprising forming the conductive metal oxide into a second capacitor electrode, and further comprising providing the second capacitor electrode to comprise titanium in addition to the conductive metal oxide.
 14. The method of claim 11 comprising forming the conductive metal oxide into a second capacitor electrode, and further comprising providing the second capacitor electrode to comprise titanium and silicon in addition to the conductive metal oxide.
 15. The method of claim 14 comprising forming the silicon to comprise both polycrystalline silicon and silicide.
 16. The method of claim 11 wherein, the first capacitor electrode is formed to comprise silicon, and further comprising rapid thermal nitridizing the first capacitor electrode and forming a silicon nitride layer, the Ta₂O₅ of the capacitor dielectric layer being formed in contact with the silicon nitride; and forming the conductive metal oxide into a second capacitor electrode, and further comprising providing the second capacitor electrode to comprise titanium and silicon in addition to the conductive metal oxide, the silicon of the second capacitor electrode comprising both polycrystalline silicon and a silicide, the titanium comprising titanium nitride, the polycrystalline silicon and being formed over the titanium nitride, the silicide being formed over the polycrystalline silicon.
 17. A method of forming a capacitor comprising: forming a first capacitor electrode over a substrate; forming a capacitor dielectric layer comprising Ta₂O₅ over the first capacitor electrode; and forming at least a portion of a second capacitor electrode over and in contact with the Ta₂O₅ in an oxygen containing environment at a temperature of at least about 175° C.
 18. The method of claim 17 comprising forming the second capacitor electrode to comprise a conductive metal oxide.
 19. The method of claim 17 comprising forming the second capacitor electrode by chemical vapor deposition.
 20. A capacitor comprising: a first capacitor electrode comprising a conductively doped Si—Ge alloy; a Si₃N₄ layer over the first capacitor electrode; a capacitor dielectric layer comprising Ta₂O₅ over the Si₃N₄ layer; and a second capacitor electrode over the Ta₂O₅ capacitor dielectric layer.
 21. The capacitor of claim 20 wherein the Si₃N₄ layer is less than or equal to about 50 Angstroms thick.
 22. The capacitor of claim 20 wherein the second capacitor electrode comprises a conductive metal oxide.
 23. The capacitor of claim 20 wherein the Si₃N₄ is formed in contact with the Si—Ge alloy.
 24. The capacitor of claim 20 wherein the Ta₂O₅ is formed in contact with the Si₃N₄.
 25. The capacitor of claim 20 wherein the Si₃N₄ is formed in contact with the Si—Ge alloy, and the Ta₂O₅ is formed in contact with the Si₃N₄.
 26. The capacitor of claim 20 wherein the second capacitor electrode comprises a conductive metal oxide, the Si₃N₄ is formed in contact with the Si—Ge alloy, and the Ta₂O₅ is formed in contact with the Si₃N₄.
 27. A method of forming a capacitor comprising: forming a first capacitor electrode comprising a conductively doped Si—Ge alloy; rapid thermal nitridizing the first capacitor electrode and forming Si₃N₄ to a thickness less than about 60 Angstroms; forming a capacitor dielectric layer comprising Ta₂O₅ over the Si₃N₄ layer; and forming a second capacitor electrodes over the Ta₂O₅ capacitor dielectric layer.
 28. The method of claim 27 comprising forming the Ta₂O₅ in contact with the Si₃N₄.
 29. The method of claim 27 comprising forming the second capacitor electrode to comprise a conductive metal oxide.
 30. The method of claim 27 comprising forming the second capacitor electrode to comprise a conductive metal oxide, the conductive metal oxide being in contact with the Ta₂O₅.
 31. A capacitor comprising: a first capacitor electrode; a capacitor dielectric layer over the first capacitor electrode; and a second capacitor electrode over the capacitor dielectric layer, the second capacitor electrode comprising a conductive silicon comprising layer, over a conductive titanium comprising layer, over a conductive metal oxide layer.
 32. The capacitor of claim 31 wherein the conductive metal oxide is in contact with the capacitor dielectric layer.
 33. The capacitor of claim 31 wherein the conductive silicon comprises polycrystalline silicon and silicide.
 34. The capacitor of claim 31 wherein the conductive silicon is formed in contact with the titanium comprising layer, the titanium comprising layer is formed in contact with the conductive metal oxide, and the conductive metal oxide is formed in contact with the capacitor dielectric layer.
 35. A method of forming a capacitor comprising: forming a first capacitor electrode over a substrate; forming a capacitor dielectric layer over the first capacitor electrode; forming a second capacitor electrode over the capacitor dielectric layer, at least one of the first and second capacitor dielectric layers comprising a conductive metal oxide and a conductive silicon; and providing a titanium comprising layer intermediate the conductive metal oxide and conductive silicon, the titanium comprising layer being provided by chemical vapor deposition using an organic precursor.
 36. The method of claim 35 comprising forming the conductive metal oxide in contact with the capacitor dielectric layer.
 37. The method of claim 35 comprising forming the conductive silicon to comprise polycrystalline silicon and silicide.
 38. The method of claim 35 comprising forming the conductive silicon in contact with the titanium comprising layer, the titanium comprising layer in contact with the conductive metal oxide, and the conductive metal oxide in contact with the capacitor dielectric layer.
 39. A capacitor comprising: a first capacitor electrode; a capacitor dielectric layer over the first capacitor electrode; and a second capacitor electrode over the capacitor dielectric layer, the capacitor dielectric layer comprising Ta₂O₅, at least one of the first and second capacitor electrodes comprising titanium, no titanium comprising material of either the first and the second capacitor electrodes being in contact with the Ta₂O₅ of the capacitor dielectric layer.
 40. The capacitor of claim 39 wherein both the first and the second capacitor electrodes comprise silicon.
 41. The capacitor of claim 39 wherein both the first and the second capacitor electrodes comprise silicon, at least one of the electrodes comprising silicon in the form of a silicide.
 42. The capacitor of claim 39 wherein both the first and the second capacitor electrodes comprise silicon, only one of the electrodes comprising silicon in the form of a silicide.
 43. The capacitor of claim 39 wherein the titanium comprises TiN.
 44. The capacitor of claim 39 wherein only one of the first and second capacitor electrodes comprises titanium.
 45. The capacitor of claim 39 wherein at least one of the first and second capacitor electrodes comprises silicon and germanium.
 46. The capacitor of claim 39 wherein only one of the first and is second capacitor electrodes comprises silicon and germanium.
 47. The capacitor of claim 39 wherein at least one of the first and second capacitor electrodes comprises a conductive metal oxide.
 48. The capacitor of claim 39 wherein only one of the first and second capacitor electrodes comprises a conductive metal oxide.
 49. A DRAM cell comprising: a first capacitor electrode; a capacitor dielectric layer comprising Ta₂O₅ over the first capacitor electrode; a second capacitor electrode over the Ta₂O₅ capacitor dielectric layer, the second capacitor electrode comprising a conductive metal oxide in contact with the Ta₂O₅; and a field effect transistor having a pair of source/drain regions, one of the source/drain regions being in electrical connection with the first capacitor electrode, the other of the source drain regions being in electrical connection with a bit line.
 50. A DRAM cell comprising: a first capacitor electrode; a capacitor dielectric layer over the first capacitor electrode; a second capacitor electrode over the capacitor dielectric layer, the second capacitor electrode comprising a conductive silicon comprising layer, over a conductive titanium comprising layer, over a conductive metal oxide layer; and a field effect transistor having a pair of source/drain regions, one of the source/drain regions being in electrical connection with the first capacitor electrode, the other of the source drain regions being in electrical connection with a bit line.
 51. A method of forming a DRAM cell comprising: forming a first capacitor electrode over a substrate; forming a capacitor dielectric layer over the first capacitor electrode; forming a second capacitor electrode over the capacitor dielectric layer, at least one of the first and second capacitor dielectric layers comprising a conductive metal oxide and a conductive silicon; providing a titanium comprising layer intermediate the conductive metal oxide and conductive silicon, the titanium comprising layer being provided by chemical vapor deposition using an organic precursor; and providing a field effect transistor having a pair of source/drain regions, one of the source/drain regions being provided in electrical connection with the first capacitor electrode, the other of the source drain regions being provided in electrical connection with a bit line. 